Acrylic resin cements 丙烯酸树脂粘接剂
Implants for surgery-Acrylic resin cements 外科植入物
Dual-cure resin cements 双固化树脂水门汀
Resin-modified glass ionomer cements 树脂改性玻璃离子水门汀
According to modified USPHS criteria after one year,the restorations which reached Alpha were 85.7% in marginal adaptation,83.9% in anatomic form,88.9% in surface texture,85.7% in color match. There was no significant difference between four types of resin cements.
4.按照USPHS标准检测结果显示,一年后86个修复体达到Alpha类标准的边缘适合性为85.7%以上,外形83.9%以上,表面质地88.9%以上,颜色匹配85.7%以上,四种树脂粘固剂间无明显差别,均达到了令人满意的结果。
参考来源 - CAD/CAM长石质全瓷修复体粘结性能的实验和临床研究·2,447,543篇论文数据,部分数据来源于NoteExpress
Resin cements have been reported to produce 150% to 200% the retention strength of zinc phosphate and glass ionomer cements.
不同粘接剂对桩的固位力大小有显著性影响,树脂粘接剂的粘接强度为玻璃离子和磷酸锌水门汀的1.5 - 2.0倍。
Objective To investigate the relationship between marginal film thickness of resin luting cements and microleakage.
目的研究树脂类粘结剂边缘厚度与全瓷冠边缘微渗漏的相关关系。